Name: 99.5%min/99.7%min ZnO Indirect Zinc Oxide CAS1314-13-2
Availability: InStock

99.5%min/99.7%min ZnO Indirect Zinc Oxide CAS1314-13-2

Our high purity Indirect Zinc Oxide 99.5%min/99.7%min is a white hexagonal crystal system powder. At room temperature, it is odorless, tasteless and non-sandy. When heated, it turns yellow and returns to its original color upon cooling. Its melting point is 1975℃ and boiling point is 2360℃. It is insoluble in water but soluble in acids, strong alkalis, ammonia water and ammonium salt solutions. It sublimates when heated to 1800℃. It is mainly used in the rubber industry (accounting for 50%), varistors, paints, feed, medicine and other fields.

Numéro de dossier :
1314-13-2
Formule moléculaire :
ZnO
Densité :
5.606 g/cm³
Point de fusion :
1975ºC
Code SH :
2817001000
EINECE N° :
215-222-5
Emballage :
25kg vowen bag
Apparence :
White or Light Yellow powder
Pureté :
99.5%min/99.7%min

Détails du produit

Basic information

The indirect method of zinc oxide distribution in rubber is uniform. It has a large contact area with hydrogen sulfide, and the interface reaction is sufficient. It can efficiently be converted into zinc sulfide, enhancing the activity of the accelerator, reducing the amount of the accelerator (about 30%), shortening the curing time (about 20%-30%), and making the curing more thorough. It also improves the thermal conductivity, wear resistance and tear resistance of the rubber.

Specification

ITEM	STANDARD		MF	ZnO
ZnO	99.5%min	99.7%min	MW	81.38
PbO	0.05%max	0.008%max	CAS NO.	1314-13-2
CuO	0.0003%max	0.0002%max	EINECE NO.	215-222-5
CdO	0.0005%max	0.0001%max	Purity	99.5%min/99.7%min
HCL	0.02%max	0.006%max	Appearance	White or Light Yellow powder
LOI	0.05%max	0.02%max	HS code	2817001000
Residue on Sieve 325μm	0.08%max	0.04%max	Density	5.606g/cm3
Water Soluble Matter	0.1%max	0.02%max	Package	25kg woven bag
Moisture	0.3%max	0.1%max	Melting Point	1975ºC

Application

1. Tire application: Indirectly applied zinc oxide is a key additive in tires (especially radial tires), enhancing thermal conductivity (aiding in heat dissipation), wear resistance (increasing lifespan), and tear resistance (improving safety), while reducing the amount of zinc oxide used (approximately 30%). Directly applied zinc oxide, due to its poor vulcanization activity, cannot meet the performance requirements of tires and is only used in low-end rubber products.

2. Transparent rubber products: High-activated zinc oxide (such as nano-zinc oxide) can replace traditional carbon black activators due to its small particle size (<100 nanometers) and good dispersion, avoiding the blackening of the products while maintaining vulcanization activity and reinforcing effect. Directly applied zinc oxide is not applicable as it contains many impurities and has large particle sizes, which would cause color changes in transparent products.

3. Special rubber products: In chloroprene rubber, zinc oxide acts as a vulcanizing agent and a thermal conductor. High-activated products can significantly improve thermal conductivity; in white latex, zinc oxide acts as a coloring agent and filler, requiring high purity (to avoid staining by impurities) and high activation degree (to ensure vulcanization effect).